类型 |
序号 |
牌号 |
化 学 成 分 % |
|
|
C |
Si |
Mn |
P |
S |
Ni |
Cr |
Mo |
Cu |
N |
其他 |
|
|
奥 |
1 |
1Cr17Mn6Ni5N |
≤0.15 |
≤1.00 |
5.50~7.50 |
≤0.060 |
≤0.030 |
3.50~5.50 |
16.00~18.00 |
- |
- |
≤0.25 |
- |
|
|
2 |
1Cr18Mn8Ni5N |
≤0.15 |
≤1.00 |
7.50~10.00 |
≤0.060 |
≤0.030 |
4.00~6.00 |
17.00~19.00 |
- |
- |
≤0.25 |
- |
|
|
氏 |
3 |
1Cr18Mn10Ni5Mo3N |
≤0.10 |
≤1.00 |
8.50~12.00 |
≤0.060 |
≤0.030 |
4.00~6.00 |
17.00~19.00 |
2.8~3.5 |
- |
0.20~0.30 |
- |
|
|
|
4 |
1Cr17Ni7 |
≤0.15 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
6.00~8.00 |
16.00~18.00 |
- |
- |
- |
- |
|
|
体 |
5 |
1Cr18Ni8 |
≤0.15 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
8.00~10.00 |
17.00~19.00 |
- |
- |
- |
- |
|
|
|
Y1Cr18Ni9 |
≤0.15 |
≤1.00 |
≤2.00 |
≤0.20 |
≥0.15 |
8.00~10.00 |
17.00~19.00 |
1) |
- |
- |
- |
|
|
型 |
6 |
Y1Cr18Ni9Se |
≤0.15 |
≤1.00 |
≤2.00 |
≤0.20 |
8.00~10.00 |
17.00~19.00 |
- |
- |
- |
Se≥0.15 |
|
|
|
7 |
OCr18Ni9 |
≤0.07 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.060 |
8.00~11.00 |
17.00~19.00 |
- |
- |
- |
- |
|
|
|
8 |
00Cr19Ni10 |
≤0.030 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
8.00~12.00 |
18.00~20.00 |
- |
- |
- |
- |
|
|
|
9 |
0Cr19Ni9N |
≤0.08 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
7.00~10.50 |
18.00~20.00 |
- |
- |
0.10~0.25 |
- |
|
|
|
10 |
0Cr19Ni10NbN |
≤0.08 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
7.50~10.50 |
18.00~20.00 |
- |
- |
0.15~0.30 |
Nb≤0.15 |
|
|
|
11 |
00Cr18Ni10N |
≤0.030 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
8.50~11.50 |
17.00~19.00 |
- |
- |
0.12~0.22 |
- |
|
|
|
12 |
1Cr18Ni12 |
≤0.12 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
10.50~13.00 |
17.00~19.00 |
- |
- |
- |
- |
|
|
|
13 |
0Cr23Ni13 |
≤0.08 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
12.00~15.00 |
22.00~24.00 |
- |
- |
- |
- |
|
|
|
14 |
0Cr25Ni20 |
≤0.08 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
19.00~22.00 |
24.00~26.00 |
- |
- |
- |
- |
|
|
|
15 |
0Cr17Ni12Mo2 |
≤0.08 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
10.00~14.00 |
16.00~18.50 |
2.00~3.00 |
- |
- |
- |
|
|
|
16 |
1Cr18Ni12Mo2Ti |
≤0.12 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
11.00~14.00 |
16.00~19.00 |
1.80~2.50 |
- |
- |
Ti5×(C%-0.02)~0.80 |
|
|
|
17 |
0Cr18Ni12Mo2Ti |
≤0.08 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
11.00~14.00 |
16.00~19.00 |
1.80~2.50 |
- |
- |
Ti5×C%-0.70 |
|
|
|
18 |
00Cr17Ni14Mo2 |
≤0.030 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
12.00~15.00 |
16.00~18.00 |
2.00~3.00 |
- |
- |
- |
|
|
|
19 |
0Cr17Ni12Mo2N |
≤0.08 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
10.00~14.00 |
16.00~18.00 |
2.00~3.00 |
- |
0.10~0.22 |
- |
|
|
|
20 |
00Cr17Ni13Mo2N |
≤0.030 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
10.50~14.50 |
16.00~18.50 |
2.00~3.00 |
- |
0.12~0.22 |
- |
|
|
|
21 |
0Cr18Ni12Mo2Cu2 |
≤0.08 |
≤1.00 |
≤2.00 |
≤2.00 |
≤0.030 |
10.00~14.50 |
17.00~19.00 |
1.20~2.75 |
1.00~2.50 |
- |
- |
|
|
|
22 |
00Cr18Ni14Mo2Cu2 |
≤0.030 |
≤1.00 |
≤2.00 |
≤2.00 |
≤0.030 |
12.00~16.00 |
17.00~19.00 |
1.20~2.75 |
1.00~2.50 |
- |
- |
|
|
|
23 |
0Cr19N13Mo3 |
≤0.08 |
≤1.00 |
≤2.00 |
≤2.00 |
≤0.030 |
11.00~15.00 |
18.00~20.00 |
3.00~4.00 |
- |
- |
- |
|
|
|
24 |
00Cr19Ni13Mo3 |
≤0.030 |
≤1.00 |
≤2.00 |
≤2.00 |
≤0.030 |
11.00~15.00 |
18.00~20.00 |
3.00~4.00 |
- |
- |
- |
|
|
|
25 |
1Cr18Ni12Mo3Ti |
≤0.12 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
11.00~14.00 |
16.00~19.00 |
2.50~3.50 |
- |
- |
Ti5×(C%-0.02)~0.80 |
|
|
|
26 |
0Cr18Ni12Mo3Ti |
≤0.08 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
11.00~14.00 |
16.00~19.00 |
2.50~3.50 |
- |
- |
Ti5×C%-0.70 |
|
|
|
27 |
0Cr18Ni16Mo5 |
≤0.040 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
15.00~17.00 |
16.00~19.00 |
4.00~6.00 |
- |
- |
- |
|
|
|
28 |
1Cr18Ni9Ti |
≤0.12 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
8.00~11.00 |
17.00~19.00 |
- |
- |
- |
Ti5×(C%-0.02)~0.80 |
|
|
|
29 |
0Cr18Ni10Ti |
≤0.08 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
9.00~12.00 |
17.00~19.00 |
- |
- |
- |
Ti≥5×C% |
|
|
|
30 |
0Cr18Ni11Nb |
≤0.08 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
9.00~13.00 |
17.00~19.00 |
- |
- |
- |
Ti≥10×C% |
|
|
|
31 |
0Cr18Ni9Cu3 |
≤0.08 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
8.50~10.50 |
17.00~19.00 |
- |
3.00~4.00 |
- |
- |
|
|
|
32 |
0Cr18Ni12Si4 |
≤0.05 |
3.00~5.00 |
≤2.00 |
≤0.035 |
≤0.030 |
11.50~15.00 |
15.00~20.00 |
- |
- |
- |
2) |
|
|
奥 |
34 |
0Cr26Ni5Mo2 |
≤0.08 |
≤1.00 |
≤1.05 |
≤0.035 |
≤0.030 |
3.00~6.00 |
23.00~28.00 |
1.00~3.00 |
- |
- |
2) |
|
|
氏 |
|
|
体 |
35 |
1Cr18Ni11Si4A1Ti |
0.10~0.18 |
3.40~4.00 |
≤0.80 |
≤0.035 |
≤0.030 |
10.00~12.00 |
17.50~19.50 |
- |
- |
- |
A1 0.10~0.30 |
|
|
铁 |
36 |
00Cr18Ni5Mo3Si2 |
≤0.030 |
1.30~2.00 |
1.00~2.00 |
≤0.035 |
≤0.030 |
4.50~5.50 |
18.00~19.50 |
2.50~3.00 |
- |
- |
Ti 0.40~0.70 |
|
|
铁 |
37 |
0Cr12A1 |
≤0.08 |
≤1.00 |
≤1.00 |
≤0.035 |
≤0.030 |
3) |
11.50~14.50 |
- |
- |
- |
A1 0.01~0.30 |
|
|
38 |
00Cr12 |
≤0.030 |
≤1.00 |
≤1.00 |
≤0.035 |
≤0.030 |
3) |
11.00~13.00 |
- |
- |
- |
- |
|
|
素 |
39 |
1Cr17 |
≤0.12 |
≤0.75 |
≤1.00 |
≤0.035 |
≤0.030 |
3) |
16.00~18.00 |
- |
- |
- |
- |
|
|
|
40 |
Y1Cr17 |
≤0.12 |
≤1.00 |
≤1.25 |
≤0.060 |
≥0.15 |
3) |
16.00~18.00 |
1) |
- |
- |
- |
|
|
体 |
41 |
1Cr17Mo |
≤0.12 |
≤1.00 |
≤1.00 |
≤0.035 |
≤0.030 |
3) |
16.00~18.00 |
0.75~1.25 |
- |
- |
- |
|
|
|
42 |
00Cr30Mo2 |
≤0.010 |
≤0.40 |
≤0.40 |
≤0.030 |
≤0.020 |
- |
28.50~32.00 |
1.50~2.50 |
- |
≤0.015 |
- |
|
|
型 |
43 |
00Cr27Mo |
≤0.010 |
≤0.40 |
≤0.40 |
≤0.030 |
≤0.020 |
- |
25.00~27.50 |
0.75~1.50 |
- |
≤0.015 |
- |
|
|
注:1)可加入小于等于0.60%钼; |
2)必要时,可添加上表以外的合金元素; |
3)允许含有小于等于0.60%镍; |
4)可以加入小于等于0.75%钼; |
5)00Cr30Mo2、00Cr27Mo允许含有小于等于0.50%镍,小于等于0.20%铜,而Ni+Cu≤0.05%,必要时,可添加上表以外的合金元素; |
6)此牌号除专用外,一般情况下不推荐使用。 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|